Ask Lemmy
A Fediverse community for open-ended, thought provoking questions
Please don't post about US Politics. If you need to do this, try !politicaldiscussion@lemmy.world
Rules: (interactive)
1) Be nice and; have fun
Doxxing, trolling, sealioning, racism, and toxicity are not welcomed in AskLemmy. Remember what your mother said: if you can't say something nice, don't say anything at all. In addition, the site-wide Lemmy.world terms of service also apply here. Please familiarize yourself with them
2) All posts must end with a '?'
This is sort of like Jeopardy. Please phrase all post titles in the form of a proper question ending with ?
3) No spam
Please do not flood the community with nonsense. Actual suspected spammers will be banned on site. No astroturfing.
4) NSFW is okay, within reason
Just remember to tag posts with either a content warning or a [NSFW] tag. Overtly sexual posts are not allowed, please direct them to either !asklemmyafterdark@lemmy.world or !asklemmynsfw@lemmynsfw.com.
NSFW comments should be restricted to posts tagged [NSFW].
5) This is not a support community.
It is not a place for 'how do I?', type questions.
If you have any questions regarding the site itself or would like to report a community, please direct them to Lemmy.world Support or email info@lemmy.world. For other questions check our partnered communities list, or use the search function.
Reminder: The terms of service apply here too.
Partnered Communities:
Logo design credit goes to: tubbadu
view the rest of the comments
Don't the lead-acid have better longetivity tho, since you can change the acid?
Yeah, I guess you could recondition one kinda like how this guy does it. I had never heard of doing that before. Thanks for the info.
I would still opt for li ion even with that though. Lithium Ion has a 2x greater depth of discharge(usable stored power) and 2-3x the lifetime (not taking into account any reconditioning) when compared to lead acid. That equals 4-6x the utility theoretically at around double the cost. That would make li ion 2-3x more bang for your buck compared to lead acid.
But there may be some case, for using a cheaper lead acid on a small scale project. Just be aware of the maintenance requirements of them and the increased cost if you do end up using it on a long term project.
The acid is not the problem. It's the sulfation of the plates (or mats) in flooded cell (and absorbent glass mat) batteries that ruins the batteries.